Iranian Journal of Materials Science and Engineering
Iran University of Science & Technology
Fri, Dec 27, 2024
[Archive]
Volume 11, Issue 4 (December 2014)
IJMSE 2014, 11(4): 8-11 |
Back to browse issues page
Download citation:
BibTeX | RIS | EndNote | Medlars | ProCite | Reference Manager | RefWorks
Send citation to:
BibTeX | RIS | EndNote | Medlars | ProCite | Reference Manager | RefWorks
Send citation to:
Parvin N, Derakhshandeh Haghighi R, Naeimi M, Parastar Namin R, Hadavi M M. EFFECT OF NICKEL AND COBALT ADDITIONS ON INFILTRATION BEHAVIOR, MICROSTRUCTURE AND HARDNESS OF W-AG COMPOSITES. IJMSE 2014; 11 (4) :8-11
URL: http://ijmse.iust.ac.ir/article-1-715-en.html
URL: http://ijmse.iust.ac.ir/article-1-715-en.html
Abstract: (25084 Views)
In this research, infiltration behavior of W-Ag composite compacts with Nickel and Cobalt as additives has been investigated. Nickel and Cobalt were added to Tungsten powder by two distinct methods: mixing elementally and reduction of salt solution. The coated Tungsten powders were compacted under controlled pressures to make porous skeleton with 32-37 vol. % porosity. Infiltration process was carried out at 1100 ̊C under a reducing atmosphere for 1h. The effect of additives on infiltration of Ag and density were evaluated by SEM and Archimedes methods. Properties of the specimens were compared following two distinct processes namely: I) sintering simultaneously with infiltration process and II) sintering prior to infiltration (pre-sintering process). It was found that specimens which were pre-sintered and then infiltrated with molten silver represent higher hardness and finer microstructure than the specimens infiltrated simultaneously with sintering.
Keywords: Infiltration, W-Ag Composites, Powder Metallurgy, Mixing Elementally, Reduction of Salt Solution