Nihel Hsouna, Mohsen Mhadhbi, Chaker Bouzidi,
Volume 19, Issue 1 (3-2022)
Abstract

Phosphate glass with different Al2O3 and Na2CO3 compositions [80NaH2PO4-(20-x) Na2CO3-xAl2O3 with a step from 0 to 4] were prepared through melt quenching technique furnace at 900 °C. In order to determine the structure and microstructure modification of the samples after heat treatment the IR and Raman spectroscopy were performed. The X-ray diffraction (XRD) result shows an amorphous character of the prepared glass. The result obtained by differential scanning calorimetry (DSC) reveals a good thermal stability in the temperature range of 25 to 400 °C. The impedance Nyquist diagrams were investigated and modeled by resistors and constant phase elements (CPE) equivalent circuits. These measurements show a non-Debye type dielectric relaxation. Both AC and DC conductivity, dielectric constant, and loss factors were determined. Thermal activation energies were also calculated. A changes in the electrical conductivity and activation energy depend upon the chemical composition were observed. Also, a transition in the conduction mechanism from ionic to mixed ionic polaronic was noted. In the same line, electrical modulus and dielectric loss parameters are also deduced. Their frequency and temperature dependency exhibited relaxation behavior. Likewise, activation energies value obtained from the analysis of M’’ and those obtained from the conductivity are closes, which proves the optimal character of the preparation conditions.

Nouar Sofiane Labidi,
Volume 19, Issue 1 (3-2022)
Abstract

The synthesed foam-shaped zeolite ZSM-5 material w:::as char:::acterized by X-ray diffraction (XRD), (FTIR) spectroscopy, scanning electron microscopy (SEM) and BET technique. The adsorption performances of the material were evaluated for the basic blue-41 dye removal. A maximum removed amount of 161.29 mg/g  at 323K was achieved. Experimental kinetic data of this new adsorbent fitted well the pseudo-second order model. The apparent diffusion coefficient values was in the range of 10-12 cm2/s. The regeneration tests revealed that the adsorption efficiency of the foam-shaped zeolite was retained after three  regeneration runs, with a loss of 6% of the original adsorbed value.
Parviz Parviz Mohamadian Samim, Arash Fattah-Alhosseini, Hassan Elmkhah, Omid Imantalab,
Volume 19, Issue 1 (3-2022)
Abstract

In this study, CrN/ZrN multilayer nanostructured coatings with different bilayers (10, 20, and 30) were created by the cathodic arc evaporation. The electrochemical behavior of samples was evaluated by polarization and impedance spectroscopy tests in the Ringer medium and the pin on disk test was used to investigate the tribological behavior of the samples. The results of measurements showed that the electrochemical and tribological behavior of the coatings depends on the number of bilayers and by rising the number of bilayers, the coating shows higher corrosion resistance and better tribological performance. Field emission scanning electron microscopy (FE-SEM) images of the specimens after exposure to the corrosion medium showed that the number of surface cavities were formed by the coating that had the highest number of bilayers comparing with other coatings were quite fewer in number and smaller in diameter. The results of the pin on disk test showed that by increasing the number of bilayers from 10 to 30, the coefficient of friction and wear rate decreased and the 30L coating ‌showed better wear resistance.
Puneeth Puneeth, Gangarekaluve J. Naveen, Vishwanath Koti, Nitrahalli D. Prasanna, Litton Bhandari, Javaregowda Satheesh, Parthasarathy Sampathkumara,
Volume 19, Issue 1 (3-2022)
Abstract

Hybrid composite finds wide application in various fields. In this present study, the hybrid composites are developed using stir casting technique as per Taguchi’s L9 orthogonal array. Hybrid composites were fabricated using Aluminium Al6082 as the base material and reinforced with the combinations of reinforcements Al2SiO5 and B4C at three levels (4%, 8% and 12%).The developed composites were analyzed for micro structural  investigations and mechanical tests were done as per ASTM standards. The micro structural analysis was done using optical Microscope and Scanning electron microscope while composition studies were done using X-ray diffraction and EDAX. Mechanical test like tensile, impact and flexural were conducted and their damage assessment was done using Scanning electron microscope. The fatigue characteristics like high cycle fatigue and fatigue crack propagation was studied both experimentally and numerically. The experimental data and numerical modeling analysis data obtained for the hybrid composite system, agree with each other.           
Saleheh Abbaspoor, Farhang Abbasi, Samira Agbolaghi,
Volume 19, Issue 2 (6-2022)
Abstract

Single crystals of double crystalline block copolymers of poly(ethylene glycol) (PEG)-b-poly(ε-caprolactone) (PCL) and PEG-b-poly(L-lactide) (PLLA) were grown from dilute solution in homo- and mixed-brush systems. Crystallization behavior of biodegradable one end-restricted crystallizable PCL and PLLA chains in homo- and mixed-brush nanostructures were investigated. Chemical and physical circumstances of crystallizable brushes were altered. Physical environment was adjusted by amorphism/crystallinity and rigidity/flexibility of neighboring brushes. Chemical environment was manipulated by interaction and miscibility of various brushes. Distinct single crystals were grown with mixed-brushes of amorphous-crystalline (polystyrene (PS), poly(methyl methacrylate) (PMMA), PCL and PLLA, double crystalline (PCL/PLLA), and rod-crystalline polyaniline (PANI)/PCL or PLLA. Surrounding was only effective on hindrance or nucleation commencement of crystallization for crystallizable brushes and had no effect on crystallization features. Novel three-layer fully single crystalline nanostructures, whose characteristics were fixed via changing the crystallization temperature, were also developed. For long crystallizable tethers, crystallization increased both brush and substrate thicknesses. 
Tashi Tenzin, Amrinder Kaur,
Volume 19, Issue 2 (6-2022)
Abstract

Green synthesis refers to the synthesis of nanoparticles using plants and microorganisms. It is preferred over conventional methods as its sustainable, eco-friendly, cost effective and rapid method. The phytochemicals and enzymes present in plants and microorganisms respectively acts as the reducing and capping agent for the synthesis of nanoparticles. Phytochemicals and enzymes have the ability to reduce precursor metal ions into nanoparticles. As the conventional methods involve the use of high energy and toxic chemicals which are harmful to both environment and organisms, these synthesis methods are discouraged. Of the nanoparticles, gold nanoparticles (AuNPs) and silver nanoparticles (AgNPs) have gained lots of attention owing to their multiple applications and less toxicity. In addition, various in-vitro studies have reported the antimicrobial activity of AgNPs and AuNPs against various microbes. This particular review portrays the methods of nanoparticles synthesis, components of green synthesis, mechanism of green synthesis, antimicrobial activity, other applications and various factors affecting the green synthesis of AgNPs and AuNPs.
Amanda C. Juraski, Márcia M. Simbara, Vera Paschon, Sônia M. Malmonge, Juliana K.m.b. Daguano,
Volume 19, Issue 2 (6-2022)
Abstract

The success of a drug delivery system relies heavily on its interaction with cells from the target tissue. The range of applications for ibuprofen-loaded chitosan (ICH) films is widening, mainly due to the biodegradability of chitosan (CH) films and ibuprofen’s safety and versatility, with a particular interest in exploring it as neural drug delivery system. In this study, CH and 12% (w/w) ICH films were prepared through the solvent cast, and characterized regarding their physicochemical composition, surface and bulk morphology, drug release profile, and cell viability of primary neurons from the rat spinal cord. Fourier transform infrared spectroscopy (FTIR) analyses demonstrated that both groups had a similar composition. According to scanning electron microscopy (SEM) images, ibuprofen particles were entrapped on the surface and inside the polymeric matrix. In vitro drug release profile indicated that release starts as diffusion within the first hours, is best fitted by the Higuchi model, and continues for at least 30 days, in agreement with the Korsmeyer-Peppas model. Therefore, ibuprofen is first released through the diffusion process of the particles found on the surface and later through a combination of diffusion and erosion of the chitosan matrix. Regarding in vitro cell viability of primary neurons, CH and ICH extracts are non-toxic, as both groups displayed cell viability over 50%. ICH films are mildly reactive in neuronal cells, but do not cause severe cell death i.e., it allowed non-cytotoxic neuronal and glial differentiation. These findings enhanced our understanding of ICH films as a safe neural drug release system to be explored.
Seyedali Seyedmajidi, Maryam Seyedmajidi,
Volume 19, Issue 2 (6-2022)
Abstract

Recently, using calcium phosphates and at the top of them, hydroxyapatite (HA) has been considered in medical and dental applications as an artificial biomaterial due to their chemical and structural similarity to the bodychr('39')s skeletal tissues such as bone and tooth. Because of reinforcement of hydroxyapatitechr('39')s mechanical and biological properties by substitution of OH- groups by F- ions to produce fluorapaptite (FA) has been proven, in this article synthesis methods, properties and medical applications of fluorapatite and its pros and cons in comparison with hydroxyapatite have been reviewed.
Silvana Artioli Schellini, Lucieni Cristina Barbarini Ferraz, Abbas Rahdar, Francesco Baino,
Volume 19, Issue 2 (6-2022)
Abstract

Biocompatible ceramics, commonly known as “bioceramics”, are an extremely versatile class of materials with a wide range of applications in modern medicine. Given the inorganic nature and physico-mechanical properties of most bioceramics, which are relatively close to the mineral phase of bone, orthopedics and dentistry are the preferred areas of usage for such biomaterials. Another clinical field where bioceramics play an important role is oculo-orbital surgery, a highly cross- and interdisciplinary medical specialty addressing to the management of injured eye orbit, with particular focus on the repair of orbital bone fractures and/or the placement of orbital implants following removal of a diseased eye. In the latter case, orbital implants are not intended for bone repair but, being placed inside the ocular cavity, have to be biointegrated in soft ocular tissues. This article reviews the state of the art of currently-used bioceramics in orbital surgery, highlighting the current limitations and the promises for the future in this field.
Hamid Ansari, Saeed Banaeifar, Reza Tavangar, Alireza Khavandi, Soheil Mahdavi,
Volume 19, Issue 3 (9-2022)
Abstract

The present study aimed to assess the effect of replacing copper as a multi-functional ingredient in the brake pad material with potassium titanate platelet (PTP) and a particular type of ceramic fiber (CF) copper-free composite. Chase dynamometer tests were conducted to compare a brake padchr('39')s tribological behavior when PTP and CF are added to the composition with that of the copper-bearing pad. The results concluded that PTP and CF demonstrated promising outcomes such as a stable coefficient of friction (COF), lower wear rate, and better heat resistance in copper-free friction composite. Scanning electron microscope (SEM/EDS) analysis was conducted to investigate the role of main elements such as Ti, Fe, K, O, and C on the formation of contact plateaus (CPs) upon the worn surface of friction composites. PTP maintained both continuous contact and smooth friction braking application of a brake pad. The uniform distribution of Ti on the wear track on the disc worn surface depicts the role of PTPs on stabilizing the friction film formation and eventually on the stability of COF.
M.j Kadhim, Fatima Allawi, M. A. Mahdi, Sami Najah Abaas,
Volume 19, Issue 3 (9-2022)
Abstract

     Zinc Oxide (ZnO) nanorods and titanium dioxide (TiO2) nanostructures thin films were prepared onto glass substrates by the chemical bath deposition (CBD) method. The ZnO was structured as nanorods (NRs) while TiO2 was formed as nanoflowers plate as confirmed by Field-Emission Scanning Electron Microscope (FESEM) images. The ZnO/Fe3O4 and TiO2/Fe3O4 nanostructures thin films were prepared via drop-casting Fe3O4 NPs onto the grown ZnO and TiO2 nanostructures thin films. The diameter of Fe3O4 NPs was deposited onto ZnO NRs thin films and TiO2 nanostructures thin films was ranged from 8nm to 59nm with dominated range between 10nm to 30 nm.  The crystalline structure of prepared samples was investigated through X-ray diffraction (XRD) method. However, the particles size of Fe3O4  was estimated  by XRD as well as FESEM images was around 22 nm. The photocatalytic activity of the as-prepared ZnO/Fe3O4 and TiO2/Fe3O4 nanostructures thin films was investigated against methylene blue (MB) dye at room temperature with a pH value of 10 under different exposure time by visible light. The photodegradation rate of MB dye by ZnO/Fe3O4 and TiO2/Fe3O4 nanostructures thin films was higher than that obtained by ZnO and TiO2 nanostructures thin films. The best photodegradation rate of MB dye was 100% after exposure time of 180 min was obtained by ZnO/Fe3O4 nanostructures thin film whereas it was 82% for TiO2/Fe3O4 nanostructures thin films after exposure time of  240 min.  
 
Behzad Pourghasemi, Vahid Abouei, Omid Bayat, Banafsheh Karbakhsh Ravari,
Volume 19, Issue 3 (9-2022)
Abstract

 
It has long been thought-provoking and challenging as well for researchers to design and produce a special low-modulus β titanium alloy such as Ti‐35Nb‐7Zr‐5Ta, representing optimal mechanical properties that is needed to successfully simulate bone tissue. In order to identify the key effects of processing pathways on the development of microstructure, Young’s modulus, and strength, a nominal Ti-35Nb-7Zr-5Ta alloy was made via casting, hot forging, homogenizing, cold rolling and finally annealing. Results from tensile test alongside microscopic and XRD analysis confirm the importance influence of processing method on fully β phase microstructure, low elastic modulus and high strength of the alloy. The specimen with post-deformation annealing at 500 °C demonstrated the Young’s modulus of 49.8 GPa, yield strength of 780 MPa and ultimate tensile strength of 890 MPa, all of which are incredibly close to that of bone, hence suitable for orthopedic implants. At temperature above 500 °C, a sharp fall was observed in the mechanical properties.

Pooyan Soroori, Saeid Baghshahi, Arghavan Kazemi, Nastaran Riahi Noori, Saba Payrazm, Amirtaymour Aliabadizadeh,
Volume 19, Issue 3 (9-2022)
Abstract

The goal of the present study is to prepare a room temperature cured hydrophobic and self-cleaning nano-coating for power line insulators. As a result, the installed insulators operating in power lines can be coated without being removed from the circuit and without the need to cut off power. For this purpose, hydrophobic silica nanoparticles were synthesized by sol-gel method using TEOS and HMDS. The synthesized hydrophobic silica nanoparticles were characterized by XRD, FTIR, SEM, and TEM analyses to investigate phase formation, particle size, and morphology. Then the surface of the insulator was cleaned and sprayed by Ultimeg binder solution, an air-dried insulating coating, as the base coating. Then the hydrophobic nano-silica powder was sprayed on the binder coated surface and left to be air-cured at room temperature. After drying the coating, the contact angle was measured to be 149o. Pull-off test was used to check the adhesion strength of the hydrophobic coating to the base insulator. To evaluate the effect of environmental factors, UV resistance and fog-salt corrosion tests were conducted. The results showed that 150 hours of UV radiation, equivalent to 9 months of placing the samples in normal conditions, did not have any significant effect on reducing the hydrophobicity of the applied coatings.
Saba Payrazm, Saeid Baghshahi, Zahra Sadeghian, Amirtaymour Aliabadizadeh,
Volume 19, Issue 3 (9-2022)
Abstract

In this research, zinc oxide quantum dots and graphene nanocomposites were synthesized via two different methods; In the first (direct) method, ZnO-graphene Nanocomposites were made mixing the synthesized zinc oxide and graphene. In the second (indirect) method, zinc nitrate, graphene, and sodium hydroxide were used to made ZnO-graphene Nanocomposites. XRD, FTIR and Raman spectroscopy analyses were used for phase and structural evaluations. The morphology of the nanocomposites w::as char::acterized by SEM. The specific surface area and porosity of the samples were characterized by BET analysis. The optical properties of the samples were investigated by photoluminescence and ultraviolet-visible spectroscopy analyses. Results showed that using graphene, increased the photoluminescence property and shifted the photoluminescence spectrum of the composites towards the visible light spectrum. The photoluminescence of the synthesized graphene-zinc oxide composite, in the visible light region, was closer to white light than that of pure zinc oxide. According to the results of BET test, the nanocomposite synthesized by direct method had a higher surface area (25.7 m2.g-1) and a higher porosity (0.32 cm3.g-1) than the nanocomposite synthesized by the indirect method with a specific surface area of (16.5 m2.g-1) and a porosity of 0.23 cm3.g-1).

Omid Sharifi, Mohammad Golmohammad, Mozhdeh Soozandeh, Mohammad Oskouee,
Volume 19, Issue 3 (9-2022)
Abstract

Li7La3Zr2O12 (LLZO) garnets are one of the promising materials as electrolytes for solid-state batteries. In this study, Li7-3xAlxLa3Zr2O12 (x= 0.22, 0.25, and 0.28) garnet is synthesized using the combustion sol-gel method to stabilize the cubic phase for higher ionic conductivity. The X-ray diffraction (XRD) results of as-synthesized powders reveal that by addition of 0.22 and 0.25 mole Al, the tetragonal phase still co-exist, whereas 0.28 mole Al addition resulted in a single cubic phase. Afterward, the as-synthesized powders are pressed and sintered at 1180°C for 10h. The hardness evaluation revealed that Al addition increases the hardness that shows better resistance against Li dendrite formation. Besides, the secondary electron microscopy results demonstrate that the dopant has not a huge impact on particle size and grain growth whereas the porosity content has been changed. Finally, the investigation of samples' electrochemical behavior reveals that the addition of Al increases the ionic conductivity of samples by increasing the density and stability of the cubic phase as well. The results declare that the 0.25 Al sample has the highest ionic conductivity. This behavior is thought to be due to the promotion of sintering and increment of bulk ionic conductivity by doping Al.
Davar Rezakhani, Abdol Hamid Jafari,
Volume 19, Issue 4 (12-2022)
Abstract

In this work, the addition of a combination of Graphene Oxide Nanoplatelets (GONPs) and Ground
Granulated Blast Furnace Slag (GGBFS) was studied as admixture in concrete. Tests on physical and mechanical
properties and chloride permeability were conducted. GGBFS was replaced with Ordinary Portland Cement (OPC)
and it was determined that GGBFS Up to 50% by weight improves the physical and mechanical properties of
concrete. GONPs with an optimal amount of 50% by weight of GGBFS were added to the concrete and the physical
and mechanical properties of the samples were determined. It was observed that the addition of GONPs was effective
in improving the mechanical strength and physical properties of specimens. The results indicated that addition of
0.1 wt.% GO and 50 wt.% GGBFS would increase the compressive strength of the concrete sample up to 42.7%
during 28 days and 46% during 90 days compared to OPC. Concrete with a combination of 0.1 wt.% GONPs and
50 wt.% GGBFS witnessed an increase in its flexural strength up to 58.5% during 28 days and 59.2% during 90
days. The results indicated that by adding 0.1 wt.% GO and 50 wt.%, concrete chloride permeability decreased
substantially 72% for 90 day cured samples compared to OPC. GONPs as an alternative to cement up to 0.1% by
weight can accelerate the formation of C-S-H gel, thereby increasing the strength and improving the resistance of
water absorption and chloride permeability. The effects of pozolanic reaction in the concrete leading to the filling
of the pores were significant factors in the proposed curtailment mechanism
Ekaterina Dmitrieva, Ivan Korchunov, Ekaterina Potapova, Sergey Sivkov, Alexander Morozov,
Volume 19, Issue 4 (12-2022)
Abstract

The article discusses the effect of calcined clays on the properties of Portland cement. An optimal method for calcining clays is proposed, which makes it possible to reduce the proportion of Portland cement clinker in cement to 60% and increase the strength characteristics from 55 MPa to 79 MPa. The study of the composition and structure of clays made it possible to select the optimal heat treatment parameters, at which the calcination products are characterized by the highest pozzolanic activity. It is shown that the use of alkali-activated calcined clays significantly increases the strength and durability of hardened cement binders compared to the composition without additives. In addition, calcined clays increase the frost resistance of cement in a 5% NaCl solution. The obtained experimental data are confirmed by thermodynamic calculations and the results of scanning electron microscopy.
Ahabboud Malika, Najwa Gouitaa, Ahjyaje Fatimazahra, Lamcharfi Taj-Dine, Abdi Farid,
Volume 20, Issue 1 (3-2023)
Abstract

In this paper, Pb1-xFex(Zr0.52Ti0.48)O3 (PFZT) nanopowders, with x from 0.00 up to 0.20, were synthesized by using the sol-gel method. The PFZT samples were characterized by X-ray diffraction (XRD), Raman spectroscopy, scanning electron microscopy (SEM), and impedance spectroscopy. According to the experimental results, PFZT combines rhombohedral and tetragonal symmetries for all the samples without a change in phase structure. The SEM investigation indicated that the grains are homogeneous with regular form and the average grain size of PFZT ceramics changed with Fe concentration. The dielectric characterizations show that the dielectric permittivity increases with increasing temperature, and the Fe amount shifts down the temperature of transition. Moreover, a dielectric resonance phenomenon is observed for all the PFZT ceramics.
Parisa Rastgoo Oskoui, Mohammad Rezvani, Abbas Kianvash,
Volume 20, Issue 2 (6-2023)
Abstract

Abstract
The effect of different heat-treatment temperatures on the magnetic, crystallization, and structural properties of 20SiO2.50FeO.30CaO (mol%) glass ceramics was studied. The initial glass was synthesized by the sol-gel method at 25  with a precursors to solvent ratio of 1/5. After aging the resulted gel for 24 h at room temperature, it was dried in an electric dryer at 110 . By heat treatment at different temperatures, different phases such as magnetite, maghemite, and hematite were crystallized in the glass. The maximum stability temperature of magnetite and maghemite were 360  and 440  respectively. By increasing the heat treatment temperature to higher than 440 , the oxidation of maghemite to hematite was occureds. The highest magnetization amount (1.9 emu/g) belonged to sample heat treated at 680 . By increasing the heat treatment temperature to 840 , the magnetization decreased to 0.8 emu/g, due to the oxidation of maghemite. By increasing the heat treatment temperature from 440  to 680 , crystalline size of maghemite was increased from 40 to 200 nm. By forther increment of temperature to 840 , the size of maghemite crystals decreased to 17nm, due to the oxidation of maghemite to hematite.
Abstract
The effect of different heat-treatment temperatures on the magnetic, crystallization, and structural properties of 20SiO2.50FeO.30CaO (mol%) glass ceramics was studied. The initial glass was synthesized by the sol-gel method at 25  with a precursors to solvent ratio of 1/5. After aging the resulted gel for 24 h at room temperature, it was dried in an electric dryer at 110 . By heat treatment at different temperatures, different phases such as magnetite, maghemite, and hematite were crystallized in the glass. The maximum stability temperature of magnetite and maghemite were 360  and 440  respectively. By increasing the heat treatment temperature to higher than 440 , the oxidation of maghemite to hematite was occureds. The highest magnetization amount (1.9 emu/g) belonged to sample heat treated at 680 . By increasing the heat treatment temperature to 840 , the magnetization decreased to 0.8 emu/g, due to the oxidation of maghemite. By increasing the heat treatment temperature from 440  to 680 , crystalline size of maghemite was increased from 40 to 200 nm. By forther increment of temperature to 840 , the size of maghemite crystals decreased to 17nm, due to the oxidation of maghemite to hematite.
 
Zahra Shamohammadi Ghahsareh, Sara Banijamali, Alireza Aghaei,
Volume 20, Issue 2 (6-2023)
Abstract

Various analysis techniques were used to investigate the effects of P2O5 on the crystallization, mechanical features, and chemical resistance of canasite-based glass-ceramics. The results showed that canasite-type crystals were the primary crystalline phase in the examined glass-ceramics subjected to the two-step heat treatment, while fluorapatite was the secondary crystalline phase in some specimens. The microstructural observations by field emission electron microscope indicated that the randomly oriented interlocked blade-like canasite crystals decreased with an increase in the P2O5 content of the parent glasses. Among the examined glass-ceramics, the Base-P2 composition (containing 2 weight ratios of P2O5 in the glass) showed the most promising mechanical features (flexural strength of 176 MPa and fracture toughness of 2.9 MPa.m1/2) and chemical resistance (solubility of 2568 µg/cm2). This glass-ceramic could be further considered as a core material for dental restorations.

 


Page 4 from 5     

© 2022 All Rights Reserved | Iranian Journal of Materials Science and Engineering

Designed & Developed by : Yektaweb