T. Ebadzadeh, S. Ghaffari, M. Alizadeh, K. Asadian, Y. Ganjkhanlou,
Volume 16, Issue 1 (3-2019)
Abstract
The densification behavior, structural and microstructural evolution and microwave dielectric properties of Li2TiO3 + xZnO (x = 0, 0.5, 1, 1.5, 2, 3, and 5 mol%) ceramics have been investigated using X-ray diffraction, Field Emission Scanning Electron Microscopy, Raman spectroscopy and microwave resonant measurement. The Maximum density of 3.33 g/cm3 was obtained in Li2TiO3 + 2ZnO ceramic at low sintering temperature of 1100˚C. SEM investigations revealed good close packing of grains when x = 2 and preferential grain growth when x ≥ 3. The maximum values of Q × f = 31800 GHz and εr = 22.5 were obtained in Li2TiO3 + 3ZnO and Li2TiO3 + 2ZnO compositions, respectively. The observed properties are attributed to the microstructural evolution and grain growth (first case) or high density of the obtained ceramic (second case).
A. R. Abbasian, M. R. Rahimipour, Z. Hamnabard,
Volume 16, Issue 4 (12-2019)
Abstract
In this work, lithium meta titanate (Li2TiO3) nanocrystallites were synthesized by hydrothermal method and subsequent heat treatment. The shrinkage of the powder compact was measured under constant heating rate in order to study the sintering behavior of the synthesized powders. Densification curves of the synthesized powders were also constructed via the dilatometry analysis and evaluated at several heating rates. Two separate methods of analytical procedure and master curve sintering were employed to determine the activation energy of the initial sintering stage. The activation energy values were estimated based on these two distinct methods as 229±14 and 230 kJ/mol respectively, consistenting with each other. Moreover, surface diffusion was determined as the dominant mechanism of densification on initial sintering of Li2TiO3 nanocrystallites.