Showing 6 results for Mg2si
Z. Sadeghian, R. Dezfulizadeh,
Volume 13, Issue 2 (6-2016)
Abstract
In situ Al2024- Mg2Si composite was fabricated by spark plasma sintering (SPS) of reactive powder. Reactive powder was obtained from mechanical alloying (MA) of elemental powders. Clad layers of in situ composite were fabricated on Al substrates by spark plasma sintering (SPS). Structural evolution during MA process and after SPS was investigated by X-ray diffractometery (XRD). Scanning electron microscopy (SEM) was utilized to study the microstructure of sintered samples. Hardness and tensile behavior of sintered samples were investigated. The results showed that SPS of mechanically alloyed unreacted powder can result in the in situ formation of Mg2Si and Mg2Al3 within the Al matrix. SPSed clad layer showed a sound and clear interface to the Al substrate with a hardness of about 140 HV. Sintered in situ composite exhibited a tensile strength of 288 MPa.
M. Hamdi, H. Saghafian Larijani, S. G. Shabestari, N. Rahbari,
Volume 17, Issue 3 (9-2020)
Abstract
Aluminum matrix composites are candidate materials for aerospace and automotive industries owing to their specific properties such as high elastic modulus (E), improved strength and low wear rate. The effect of thixoforming process on the wear behavior of an Al-Mg2Si composite was studied in this paper. During applying thixoforming process, casting defects such as macrosegration, shrinkage and porosity are being effectively reduced. These advantages are sufficient to attract more exploration works of thixoforming operation. Thermal analysis of the composite, as-cast microstructure, wear surface and subsurface area of the thixoformed alloy were investigated. Wear behavior of the specimens were examined using a pin-on-disk machine based on ASTM-G99, at the applied loads of 25, 50 and 75 N and the constant sliding velocity of 0.25m/s. The worn surfaces and subsurfaces were examined by scanning electron microscopy (SEM). The experimental results indicated that the thixoformed specimens exhibited superior wear resistance than the as-cast alloy. Moreover, the dominant wear mechanism is an adhesive wear followed by the formation of a mechanical mixed layer (MML). However, a severer wear regime occurs in the as cast specimens compared with the thixoformed ones
Zahra Rousta, Esmaeil Tohidlou, Hamed Khosravi,
Volume 18, Issue 1 (3-2021)
Abstract
This study deals with the effects of erbium (Er) addition on the microstructural evolution and tensile properties of Al-Mg2Si in-situ metal matrix composites. The morphology of primary Mg2Si and eutectic phases were observed in details using optical microscope and scanning electron microscopy (SEM). The results showed that the increase of Er content has a slight effect on the size and morphology of primary Mg2Si phases, but the eutectic structure evolves from the coarse structure into the fine one. Also, with Er addition the eutectic mixtures of Al and Mg2Si with fibrous morphology has been developed instead of the flake like Al-Mg2Si eutectic microstructure. Meanwhile, Al3Er phase was observed in the samples containing Er. The ultimate tensile strength (UTS) of the composite changes under the various content of Er. The maximum strength was found at the 0.6 wt% Er with the fine eutectic microstructure. The study of SEM micrographs from the fracture surface of composites revealed that Er addition changes the fracture mode from brittle to ductile one with fine dimples. The mechanism of microstructural evolution was discussed in details.
Saeed G. Shabestari, Sahar Ashkvary, Farnaz Yavari,
Volume 18, Issue 3 (9-2021)
Abstract
The influence of melt superheating treatment on the solidification characteristics and microstructure of Al–20%Mg2Si in-situ composite has been investigated. The results revealed that melt superheating temperature has a significant effect on solidification parameters and morphology of primary Mg2Si particles. Solidification parameters acquired using cooling curve thermal analysis method, indicate that both nucleation temperature and nucleation undercooling of primary Mg2Si particles increase by increasing melt superheating temperature, while recalescence undercooling decrease under the same condition. Also, based on the microstructural evaluations, melt superheating treatment can refine primary Mg2Si particles and alter their morphology from dendritic shape to more spherical shape and the eutectic microstructure of a-Al + Mg2Si becomes finer and the distance between eutectic layers becomes smaller.
Amirhossein Kazemi, Arash Fattah-Alhosseini, Maryam Molaei, Meisam Nouri,
Volume 19, Issue 2 (6-2022)
Abstract
In this study, for the first time, the Forsterite (Mg2SiO4) nanoparticles (NPs) with the size of about 25 nm were added to the phosphate-based electrolyte, and the characteristics and properties of the obtained plasma electrolytic oxidation (PEO) coating on AZ31 Mg alloy was investigated. The results of the potentiodynamic polarization measurements revealed that after one week of exposure to simulated body fluid (SBF) solution, the coating with Mg2SiO4 NPs possessed 12.30 kΩ cm2 polarization resistance, which was more than two times greater than that of the coating without NPs. The thicker coating layer, lower wettability, and also presence of Mg2SiO4 NPs inside the pores were responsible for enhanced corrosion protection in the Mg2SiO4 NPs incorporated coating. After three weeks of immersion in SBF solution, the in-vitro bioactivity test results indicated the ability of the NPs-containing coating to form apatite (Ca/P ratio of 0.92) was weaker than the coating without NPs (Ca/P ratio of 1.17). This could be attributed to the lower wettability of the coating with NPs and supports that the addition of the nanoparticles is not beneficial to the bioactivity performance of the coating.
Mohammad Alipour,
Volume 20, Issue 1 (3-2023)
Abstract
The effect of Strain-Induced Melt-Activated (SIMA) Process, ultrasonic treatment (UST) and Al-5Ti-1B refiner on the microstructure and globularity of Al–15%Mg2Si composite was studied. Deformation of 25% were used. After deformation the samples were heated at 560, 580 and 595 °C for 5, 10, 20 and 40 min. The composite was treated with different amounts of the Ti concentrations and ultrasonic treatment with different power. Microstructural study was carried out on the alloy. It was observed that SIMA process, ultrasonic treatment and Al-5Ti-1B refiner has caused the globular morphology of Mg2Si particles. The results showed that for the desired microstructures of the alloy during SIMA process, the optimum temperature and time are 595 °C and 20 min respectively. Optimum amount of Ti refiner is 1 wt.% and power for UST is 1800W. After applying the SIMA process, Al-5Ti-1B master alloy and ultrasonic treatment, the strength and engagement have increased. This means that tensile strength increases from 251 MPa to 303 MPa and elongation percentage improves from 2.1 to 3.4, respectively.