The synthesis of mesoporous CuFe2O4 spinel by several nanocasting strategies (i.e., multi-step nanocasting, one step nanocasting, modified solid-liquid), in which copper and iron nitrates are used as precursors and Pluronic P123 as surfactant, is explored. We have also checked the effect of pH, citric acid and sodium citrate in multi-step nanocasting method. The modified solid-liquid method which contains impregnating mesoporous silica by molten state salts in a non-ionic solvent seems to be the best choice to obtain single phase ordered mesoporous copper ferrite. Other methods suffer from the presence of copper oxide or hematite as impurities or lack of integrity in the mesoporous structure. Increasing pH up to 9.5 does not enhance the phase formation inside the pores of the silica matrix. The citric acid yields a fine structure but does not facilitate the phase formation. Adding sodium citrate neither heals the phase formation nor the structure of the final product. Moreover, vinyl- functionalized mesoporous silica exploited in this study as a hard template entraps both metal nitrates in the pores, assisting impregnation procedure

---

In this research, a nickel-tungsten coating as a catalyst for hydrogen evolution reaction (HER) with different current densities was synthesized and the resulting electrocatalytic properties and morphology were assessed. Linear sweep voltammetry (LSV), electrochemical impedance spectroscopy (EIS), and chronoamperometry in 1 M NaOH were used to evaluate the electrocatalytic activity for HER. By increasing the current density of electrodeposition up to 500 mA/cm², a columnar morphology was observed. The cyclic voltammetry test (CV) revealed that when the plating current density increases, C_dl has increased from 248 to 1310 µF/cm² and the active surface area increases 5 times. The results showed that by modifying the coating morphology, the current density of the hydrogen evolution increased up to two times.