M. Ghasemian Safaei, Dr. S. Rastegari, R. Latifi,
Volume 17, Issue 2 (6-2020)
Abstract

In this study, Si-modified aluminide coating on nickel-base superalloy IN-738LC was prepared using a pack cementation method with various powder compositions at 1050 °C for 6 h. The cyclic oxidation test was conducted at 1000 °C followed by cooling at room temperature for 200 h and 20 cycles. The effect of powder composition and the way of cooling on the coatings microstructure and oxidation behavior were studied. Investigations carried out using a scanning electron microscope (SEM), EDS analysis, and XRD. Microstructural observations revealed that the coating thickness of 293 and 274 µm was achieved in the case of using pure Al and Si powder and alloyed Al-20wt.%Si one in the packed mixture, respectively. It was also found that utilizing pure Al and Si powder with NH4Cl as an activator in the pack led to the formation of silicide coating, owing to the higher diffusion of Si, which showed superior cyclic oxidation performance.

Sajad Ghaemifar, Hamed Mirzadeh,
Volume 20, Issue 4 (12-2023)
Abstract

Phase transformations and the evolution of hardness during elevated-temperature annealing of Inconel 718 superalloy manufactured by the laser powder bed fusion (L-PBF) were investigated. The microstructural evolution, elemental analysis, phase formation, and hardening were characterized by scanning electron microscopy, energy-dispersive spectroscopy, X-ray diffraction, and Vickers indentation test, respectively. It was observed that the effect of annealing treatments is directly governed by the annealing parameters (i.e. time and temperature), for which the hardness measurement as a fruitful and convenient tool can reveal this effect. The increase of the hardness, which was obtained by the annealing (aging) treatments at the temperature range of 800-900 °C, indicated precipitation of the Ni3Nb γ˝ strengthening phase; while owing to the coarsening of precipitates as a results of overaging at this temperature range, the hardness decreased. For instance the length and aspect ratio of precipitates in the aged sample at 800 °C for 1 h is 67.14 nm and 0.32, respectively; while these values in the aged sample at 800 °C for 8 h is 78.34 nm and 0.44, respectively. On the other hand, the decrease of the hardness at temperatures of 950 and 1000 °C was attributed to the decrease of dislocation density in conjunction with the Ni2Nb Laves phase dissolution. Hence, it is crucial to determine the annealing parameters according to the required microstructure and properties.

Page 1 from 1     

© 2022 All Rights Reserved | Iranian Journal of Materials Science and Engineering

Designed & Developed by : Yektaweb