Alishavandi M, Ebadi M, Kokabi A H. Optimization of Parameters for the Friction Stir Processing and Welding of AA1050 Aluminum Alloy. IJMSE 2021; 18 (2) :1-11
URL: http://ijmse.iust.ac.ir/article-1-2016-en.html
Abstract:   (12916 Views)
Friction-Stir Processing (FSP) was applied on AA1050 Aluminum Alloy (AA) to find the highest mechanical properties among 28 combinations of the rotational and traverse speed (800-2000 rpm and 50-200 mm.min-1) and four different tool probe shapes (threaded, columnar, square and triangle). To this aim, the AA standard sheet went through a single pass of FSP. The 1600 rpm and 100 mm.min-1 with threaded tool probe was chosen as the best combination of rotational and traverse speed. Grain size at the Stirred Zone (SZ) was studied using Optical Microscopy (OM). The results showed that the SZ’s grain size was refined from 30 μm down to about 12 μm due to dynamic recrystallization during FSP. The processed sample exhibited improved hardness, yield stress, ultimate tensile strength, elongation up to 65, 80, 66, and 14%, respectively, compared to the annealed AA sample. Studying fractographic features by OM and field emission scanning electron microscope (FESEM) revealed a dominantly ductile fracture behavior.
Full-Text [PDF 5042 kb]   (6967 Downloads)    
Type of Study: Research Paper | Subject: Ceramics

Add your comments about this article : Your username or Email:
CAPTCHA

Send email to the article author


Rights and permissions
Creative Commons License This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License.

© 2022 All Rights Reserved | Iranian Journal of Materials Science and Engineering

Designed & Developed by : Yektaweb